| Characteristics | Standards | Requirements | Result |
| TUV Premium Certification | Belgian VOC regulation BREEAM Exemplary Level | Refer to Standards | Pass |
| CE Certification | EN14041 | Refer to Standards Pass | Pass |
| Floorscore Certification | SCS-EC10.3-2014v3.0 | Refer to Standards Pass | Pass |
| Castor Chair Resistance | NALFA LF 01-2011 Section 3.9 | N/A | After 25000 cycles, test specimens no visible damage |
| Dimensional Stability | ASTM F2199-09(2014) Heating temperature: 65°C | <0.25% | MD=0.092% AMD=0.030% |
| Pentachlorophenol (PCP) | With reference to PD CEN/TR 14823-2003 | N/A | Free |
| Formaldehyde Emission | EN 717-1:2004 | E1<0.124MG/M3 | Frees |
| Free resistance | EN ISO 9239-1 EN ISO 11925-2 EN 13501-1:2010 | N/A | Bfl-s2 |
| Impact insulation | ASTM E2179-09 | N/A | IICc-28=△IIC 24 |
| Impact resistance | ASTM F1265-03A(2013) | N/A | No crack |
| Phthalate tests (DBP/BBP/DEHP/DINP/DNOP/DIDP) | REACH NO.1907/2006 | N/A | Free |
| Resistance to Heat | ASTM F1514-03(2013) | △E* shall not greater than 8.9 after 7 days exposure to 70°C | △E*=0.66 |
| Residual indentation | ASTM F1914-07(201) | Average ≤8% Max ≤10% | Average≤6.6% Max≤7.4% |
| Slip resistance | EN 13893:2003 | EN 14041: m ≥0.3 | m = 0.36 Class DS |
| Density | ASTM D792-13 Method A, Water at 23 °C | N/A | 1.15g/cm3 |
| Squareness | ASTM F2055-17 | ≤0.25mm/305mm | Short edge Max.=0.05mm/180mm |
| Size | ASTM F2055-17 | A tolerance of ±0.4mm/305mm | Pass |
| Thickness | ASTM F386-17 | A tolerance of ±0.13mm | Pass |
| Thermal Conductivity | ASTM C518-10 | N/A | 0.114 W/(m/K) |
| Thermal Resistance | ASTM C518-10 | N/A | 0.062(m2.K)W |
| TVOC | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | <1000 ug/m3 | 112 ug/m3 |
| TVOC | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤100 ug/m3 | <5 ug/m3 |
| Total VOC without LCI(D) | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤100 ug/m3 | <5 ug/m3 |
| R-Value(LCI(D))* | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤1 ug/m3 | 0.055 ug/m3 |
| Formaldehyde | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | <60 ug/m3 | <6 ug/m3 |
| Acetaldehyde | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤200 ug/m3 | 1 ug/m3 |
| Toluene | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤300 ug/m3 | 38 ug/m3 |
| Tetrachloroethylene | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | <350 ug/m3 | n.d. |
| Xylene | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | <300 ug/m3 | n.d. |
| 1,4-Dichlorobenzene | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | <90 ug/m3 | n.d. |
| Styrene | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | <350 ug/m3 | 3 ug/m3 |
| Trichloroethylene | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤1 ug/m3 | n.d. |
| DEHP | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤1 ug/m3 | n.d. |
| DBP | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤1 ug/m3 | n.d. |
| Carcinogenic substances | ISO 1600 parts-3,-6,-9,-11 Concentration after 28 days | ≤1 ug/m3 each | n.d. |
| TUV Premium Certification | Belgian VOC regulation BREEAM Exemplary | Refer to Standards | Pass |
| DIBT Certification | EN14041 | Refer to Standards | Pass |
| CE Certification | EN14041 | Refer to Standards | Pass |
| Floorscore Certification | SCS-EC10.3-2014v3.0 | Refer to Standards | Pass |
| Wear resistance | EN660-2:1999+A1:2003 EN649 2011 | N/A | Fv=1.4mm2 Wear group:T |
| Abrasion resistance (0.4mm wearlayer) | EN13329:2016 | >4000 cycles | 4300 cycles Abrasion Class: >AC4 |
| Staining resistance | EN423:2001 | N/A | Not affected |
| Chemical Solution | EN423:2002 | N/A | Not affected |
| Colour fastness to light | ISO 105 b02:1994 /Amd 1:1998+Amd 2:2000 | N/A | Grade 6 |
| Peel resistance | EN 425:2002 ISO4918:2016 | N/A | Upper layer: (X direction:90N/50mm, Y direction:90N/50mm) |
| Thermal conductivity | EN 12667:2001 | N/A | No visible damage |
| Thermal Resistance | EN 12667:2001 | N/A | 0.14 W/(m.K) |
| Slip resistance | DIN 51130:2010 EN13893 | Coefficient of Friction ≥ 0.30 | 0.03(m2.K)/W |
| Fire resistance | EN 9239-1 EN ISO11925-2 EN 13501-1 | Critical Flux f≥8.0kW/m2 Fs ≤150mm within 20s Smoke ≤750% minutes | Bfl-S1 |
| Determination of residual indentation after static loading | EN433:1994 GB/T4085-2015 | N/A | 0.038mm Pass 0.04mm |
| Impact sound insulation | ASTM E2179-09 ASTM E492-09 ASTM E989-06 | N/A | △Lw=8dB, C1, △=4dB |
| Impact insulation class | ISO 10140-1:2010 ISO 717-2:1996+A1:2006 | N/A | IIC c-28= △IIC 19 ICC 53 |
| PVC resin Stabilizer Wear layer | US EPA 8270D:2007 DMF(N,N-dimethylformamide) | N/A | Free |
| Dimensional stability and curling after exposure to heat | EN 434:1994 | ≤0.25% The curling ≤2mm | variation of X direction :-0.13% variation of Y direction :-0.12% Curling :0.071 |
| Dimension Stability Loose lay | ASTM F2199-09(R2014) | N/A | MD:=0/051 AMD:=0.071 |
| Water Absorption | ASTM D570-98(2010) | N/A | 0.17% Pass |
| Locking Strength 3.2mm thickness | ISO 24334:2014 | N/A | Longitudinal joint Maximum locking strength F max (N)=398 Transverse joint Maximum locking strength F max (N) 354 |
| Phthalate tests (DBP/BBP/DEHP/DINP/DNOP/DIDP) | EN 14372:2004 REACH NO.1907/2006 REACH NO.552/2009 | N/A | Free |
| Formaldehyde Emission | EN717-1:2004 | E1≤0.12mg/m3 | Free |
| Soluble heavy metal contents test | EN 71 Part 3:1994+ A1:2000+AC:2002 ASTM F 963-11 | N/A | Free |
| SCHV Released | EU REACH Regulation No. 1907/2006 Article 33 | N/A | Not Detected |